Example of direct smelting process of Yunxi Yiye tin concentrate without pre-baking

With this rule a cloud tin production process, dispersed in acetic arsenic, tin, and methyl tin hard head. The slag precipitated by ethylene tin, the hard head after the melting, and the condensate slag (pot residue) refined by the tin-tin fire method are all high in arsenic (see table ); in order to recover the tin and lead , the arsenic must be calcined first. . The calcined soot is enriched with arsenic (see table ) and is purified by electrothermal rotary kiln to be 95% to 99.5% white arsenic series products. The main equipment and technical conditions for the production of white arsenic by Yunxi Yiye are as follows:
Main equipment electric heating rotary kiln        ¢ 80 0 × 8000, 1 set, motor power 189 kW
Disc feeder        ¢ 1200 , 2
sets
    1 to 5 series condenser    9.5 m × 2 m × 2m , 2 sets of bag filter        26m 2 , 1 water bath precipitator        ¢ 1200, 1 high-pressure centrifugal fan      H = 0.05066 ~ 0.05333 MPa , Q = 148 5 ~ 1790 M 3 / h, 3 sets of rotary kiln firing technology pressure conditions    — 1 0 ~ — 20 Pa
Calcination temperature          40 0 ~ 1000 °C ,
Kiln speed              0.2 5 ~ 0.29 r / min ,
Feed amount            0. 9 ~ 2.0 t / h ,
Roasting slag containing arsenic        1.2 % to 4.0 %
Electric rotary kiln temperature    70 0 ~ 750 °C ,
pressure              — 2 0 ~— 40 Pa,
Kiln speed              1 to 2 r/min,
    Reduction with coal        0.5 % to 1%

  The materials of arsenic roasting and the content of soot produced by the rotary tin smelting

Calcined in the kiln
Material name
Material component / %
Sn
Pb
Zn
Cu
As
Sb
S
Fe
Ethylene tin slag
Hard head after melting
Arsenic slag
35~38
28~32
18~20
3~5
3~5
1~2
0.6~0.8
0.6~0.8
0.1~0.3
0.2~0.5
0.2~0.5
0.3~0.6
12~14
9~11
20~30
0.01~0.04
0.01~0.02
0.01~0.05
3~4
3~8
0.3~0.5
30~32
32~36
Produced soot category
Smoke component / %
As 2 O 3
Sn
Pb
Cu
Sb
S
FeO
Al 2 O 3
Settlement dust
Cyclone dust
Electric dust collection
60~75
75~85
55~75
10~25
6~12
8~12
2~3
1~2
1~2
<0.4
<0.5
<0.4
<0.07
<0.05
<0.06
<0.25
<0.2
<0.2
<0.12
<0.09
<0.09
<0.06
<0.05
<0.05

Tin Box

1. Good mechanical performance: compared with other packages, tin cans have much higher strength, good rigidity and are not easy to crack. It can be used not only for small sales package, but also for large transport package.

2. Excellent sealing performance: tinplate cans have superior sealing performance than any other materials. They are resistant to air, moisture, light and taste, and are reliable in sealing, which can protect the product to the maximum extent.


3. Mature process: The production process of tinplate cans appeared very early, its process is quite mature, and its supporting production equipment and tools are also mature, so that the production efficiency can be improved to a greater extent, and the packaging needs of various products can also be met.


4. Fine offset printing: the printing performance of metal materials is far better than that of other materials; Logo, design, text, etc. are very delicate and mellow in printing, which can effectively avoid paint falling and color fading.

5. Different shapes: tin cans can be made into various shapes according to different needs, such as square cans, oval cans, round cans, horseshoe shaped cans, trapezoidal cans, octagonal cans, etc., which not only meet the packaging needs of different products, but also make the packaging of tin cans more varied.